关键词：合金；尖晶石；不锈钢；表面处理；涂料
摘 要：Ferritic stainless steels are promising candidates for IT-SOFC interconnect applications due to their low cost and resistance to oxidation at SOFC operating temperatures. However, steel candidates face several challenges, including long term oxidation under interconnect exposure conditions, which can lead to increased electrical resistance, surface instability, and poisoning of cathodes due to volatilization of Cr. To potentially extend interconnect lifetime and improve performance, a variety of surface treatments were performed on AISI 441 ferritic stainless steel coupons prior to application of a protective spinel coating. The coated coupons were then subjected to oxidation testing at 800 and 850 degrees C in air, and electrical testing at 800 deg C in air. While all of the surface-treatments resulted in improved surface stability (i.e., increased spallation resistance) compared to untreated AISI 441, the greatest degree of improvement (through 20,000 hours of testing at 800 deg C and 14,000 hours of testing at 850 deg C) was achieved by surface blasting.